Descrição Geral
H-PLA - HIGH TEMPERATURE RESISTANCE (100 °C) | ||||
Temperature resistant 100 ° C. High toughness. Bright surface and very good smoothness. |
||||
Color: |
White | |||
Diameter (mm): | 1.75 | |||
Recommended Printing Temperature (°C): | 200-240 | |||
Recommend Heatbed Temperature (°C): | 60-80 or no heating | |||
Weight (Kg): | 1.0 | |||
Properties | ASTM | Test Condition | Units | Typical Values |
MECHANICAL PROPERTIES | ||||
Tensile Strengh | D638 | 50mm/min | MPa | 52 |
Elongation | D638 | 50mm/min | % | 4.0 |
Flexural Strength | D790 | 2mm/min | MPa | 83 |
Flexural Modulus | D790 | 2mm/min | MPa | 4000 |
lmpact Strength, 12OD notched | D256 | 3.2mm, 23'C | J/m | 50 |
lmpact Strength, 12OD notched | D256 | 3.2mm, 23'C | J/m | 450 |
THERMAL | ||||
Heat Distortion Temp. | D648 | 0.451MPa, 6.4mm | °C | 85- 110 |
OTHERS | ||||
Melt Flow Rate | D1238 | 190°C , 2.16kg | g/10min | 13 |
Specific Gravity | D792 | 23°C | g/cm3 | 1.29-1.33 |
Mold Shrinkage | D955 | 23°C | % | 0.4-1.0 |