FILAMENTO T-PLA ( + RIGIDEZ E RESISTÊNCIA ) IMPRESSÃO 3D
Toughening Polylactic Acid
Modified Polylactic Acid/Polylactide-T-PLA (Premium quality, highly)
Modified PLA, 6 times more tough than normal PLA, with high impact resistance.
Not easy to break easily, print the finished product with very smooth surface.
Color: White
Diameter (mm):1.75
Recommended Printing Temperature (°C):190-230
Recommend Heatbed Temperature (°C): 0-40
Weight (Kg):1.0
FEATURES APPLICATIONS
• Enviromnent friendly and biodegradable • Product models
• Low shrinkage, excellent dimensional stability • Art erans
• Excellent impacl resistence • Adornments
Properties Test Standart Test Condition S.I S.I Typical value ( Printing/Injection Moulding)
Physical properties
Density ISO 1183 23°C g/cm³ 1.20
Glass transition temperature ISO 11357 10°C/min °C 60
Melt index ISO 1133 190°C, 2,16kg g/10min 4.5
Mechanical properties
Tensile strength ISO 527 50mm/min MPa 34.5 46.8
Elongations break ISO 527 50mm/min % 4.1 230.5
Bending strength ISO 178 2m/min MPa 61.2 73.5
Bending modulus ISO 178 2m/min MPa 2010 2325
Izod impact notched ISO 180 23°C KJ/m² 14.5 20.5
Thermal properties
Heat distortion temperature ISO75 0.45 MPa °C 53
Flammability UL94 1.6mm Class HB
[1] Thes are typical values of the product properties, and these values alone do not represent a sufficient basis for any part
design and are not intended for use in establishing maximum, minimum, or ranges osf values for especification purposes.
[2] The lieted values are maybe different for pigmented material
Printing conditions:
Printing temperature: 210°C
Printing speed: 80mm/s
Number of shells: 2
Nozzle size: 0.4mm and 100% infill
Injection molding processing condition
temperature 190°C back pressure 0-1 MPa mould temperature 30-40°C
Typical Conditions of Printing
Printing recommendation Typical range
Extruder temp 190-230
Printing speed 30-100mm/s
Bed temp room temp - 40
Layer height 0.1 - 0.4mm
Infill as need up to 100%
Matters need attention general print
The parameter is just for referencial purpose only. In actual processing the parameter should be adjusted by
constructin of 3D machine, shape and size of product, and so on.